Comparison of Sb and Sr on modification and refinement of Mg2Si phase in AZ61-0.7Si magnesium alloy

来源 :中国有色金属学会会刊(英文版) | 被引量 : 0次 | 上传用户:zhangzhennan6
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The effects of Sb and Sr on the modification and refinement of Mg2Si phase in an AZ61-0.7Si magnesium alloy were investigated and compared. The results indicate that the difference of Sb and Sr in the modification and refinement of Mg2Si phase is significant. Addition of 0.4%Sb (mass fraction) to AZ61-0.7Si alloy can refine but not modify Mg2Si phase. Oppositely, by addition of 0.12%Sr to AZ61-0.7Si alloy, the Mg2Si phase changes from initial coarse Chinese script shape to fine granule and/or irregular polygonal shape. Accordingly, the Sr-modified AZ61-0.7Si alloy exhibits higher tensile and creep properties than the Sb-modified one. The difference of Sb and Sr in the modification and refinement of Mg2Si phase is possibly related to the following two aspects: 1) the disregistry at (100)Al4Sr//(100)Mg2Si is lower than that at (0001)Mg3Sb2//(111)Mg2Si (0.69% vs 1.72%) and 2) the onset crystallizing temperature of the Sr-modified AZ61-0.7Si alloy is lower than that of the Sb-modified one (603.1 ℃ vs 606.9 ℃).
其他文献
The Co3O4/acetylene black composite anodes were successfully prepared by combination of oxalate precipitation and pyrolysis of the precipitate. The composite an
Using rolling-ploughing-extrusion compound processing methods, a 3D integral-fin structure on outside surface of red copper tube with diameter of 16.0 mm and wa
Micrometer and nanometer Cr particles were co-deposited with Ni by electroplating from a nickel sulfate bath containing a certain content of Cr particles. Cr mi
La0.7-xSmx+0.02Ca0.3CrO3-δ(0≤x≤0.4) powders with A-site excessive perovskite structure were synthesized by auto-ignition process and characterized. X-ray dif
This investigation deals with the observations pertaining to the effects of specimen and slurry compositions as well as traversal distance on the slurry wear re
Commercial cathode material (LiCoO2) was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery
The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensi
An axisymmetrical unit cell model was used to represent a bimodal Al alloy that was composed of both nano-grained (NG) and coarse-grained (CG) aluminum. Effects
Nanocrystalline Cu with average grain size of 22.8-25.3 nm was prepared by vacuum-warm-compaction method. Scanning electronic microscope, HMV-2 type microhardne
The upconversion emission spectra of Er3+ doped oxyfluoride tellurite glasses excited by 808 nm laser diode (LD) were measured. The dependence of 550 nm upconve