采用熔铸和快凝技术制备过计量比AB5.6型储氢合金La0.8Ce0.2Ni4.65-xMn0.9Ti0.05(V0.3Fe0.4Al0.3)x(x=0~1.0),研究了(V0.3Fe0.4Al0......

用真空电弧熔炼和热处理(1000℃×10h)制备了过计量比CaCu5型结构储氢合金La0.55Ce0.25Y0.2Ni4.24Fe0.35Al0.06Mn0.95,研究了......