【摘 要】
：
The effect of H2S content on corrosion behavior of X70 pipeline steels in water-unsaturated(2500 ppmv)supercritical CO2 system containing 1000 ppmv O2 was investigated by means of weight loss tests,SE
【机 构】
：
School of Mechanical and Electronic Engineering,China University of Petroleum,Qingdao 266580,PR Chin
【出 处】
：
国际腐蚀工程大会(ICEC2016)
论文部分内容阅读
The effect of H2S content on corrosion behavior of X70 pipeline steels in water-unsaturated(2500 ppmv)supercritical CO2 system containing 1000 ppmv O2 was investigated by means of weight loss tests,SEM,EDS and XRD.
其他文献
The microbiologically influenced corrosion was investigated in the early failed copper pipes by pitting used in underground water.The bacteria were cultured by sampling from corrosion product near pit
In this work,the passivation behavior and galvanic corrosion of 304 stainless steel elbow under erosion-corrosion(E-C)condition were studied by array electrodes technique through a loop system.
The corrosion behavior and mechanism of under deposit corrosion of ammonium chloride salt of 10# carbon steel under various temperatures and relative humidity were investigated by the weight loss meth
With wide application of electronic products,they are becoming an indispensable part of our life.The service life of electronic components is attracting more and more attention.
Stress corrosion cracking(SCC)is a common type of equipment failure in chemical industry,especially for stainless steels equipment.However,many end users are not familiar with this failure mode when i
Biocorrosion,also known as microbiologically influenced corrosion(MIC),is a major problem in the oil and gas industry as well as many other industrial sectors.
The failure of an air preheater is investigated in this paper.Deposit samples and corroded heating elements were taken from the air preheater of a 300MW coal-fired power plant in Wuhan Province,China,
In a static environment,based on the heat erosion test by immersing in molten salt and electrochemical test of the heat erosion of the molten salt,the corrosion properties of the 316L,321H,P91,12CrMoV
Microbial corrosion is a major corrosion related problem for steel pipelines.There is an urgent need for oil industry to develop environmentally friendly strategies for microbial corrosion control.
Metallic oxide(scale)inevitably generates on the surface of steel strip due to thermal oxidation at elevated temperatures in corrosive environments.This sort of oxide scale can therefore cause the sur