Zirconium oxide (ZrO2) and boron carbide (B4C) were added to ZrB2 raw powders to prepare ZrB2 porous ceramics by reactive spark plasma sintering (RSPS). The reactions between ZrO2 and B4C which produce ZrB2 and gas (such as CO and B2O3) result in pore for
【机 构】
：
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Zirconium oxide (ZrO2) and boron carbide (B4C) were added to ZrB2 raw powders to prepare ZrB2 porous ceramics by reactive spark plasma sintering (RSPS). The reactions between ZrO2 and B4C which produce ZrB2 and gas (such as CO and B2O3) result in pore formation. X-Ray Diffraction results indicated that the products phase was ZrB2 and the reaction was completed after the RSPS process. The porosity could be controlled by changing the ratio of synthesized ZrB2 to raw ZrB2 powders. The porosity of porous ceramics with 20 wt% and 40 wt% synthsized ZrB2 are 0.185 and 0.222, respectivly. And dense ZrB2-SiC ceramic with a porosity of 0.057 was prepared under the same conditions for comparison. The pores were homogeneously distributed within the microstructure of the porous ceramics. The results indicate a promising method for preparing porous ZrB2-based ceramics.
其他文献
A micromechanical model based on discrete element method (DEM) was employed to investigate the effects of aggregate size and specimen scale on the cracking behavior of asphalt mixture. An algorithm for generating three-dimensional aggregates that can refl
Double-scale model for three-dimension-4 directional(3D-4d) braided C/SiC composites has been proposed to investigate its elastic properties. The double-scale model involves micro-scale that takesfi ber/matrix/porosity infi bers tows into consideration wi
The objective of this work is to study the synthesis of copper-alumina nanocomposites using the coprecipitation process and hot-pressing method, and investigate their mechanical properties. The effects of calcination temperature on the average size of com
IR Li2Ga2GeS6 nonlinear crystals were directly obtained with the composition of 40GeS2-30Ga2S3-30Li2S, by the conventional melt-quenching method. The high depth digital image indicated that the obtained Li2Ga2GeS6 crystals showed a big size of 0.3 × 0.25
The aim of this work was to prepare MgF2 translucent ceramic by using nanopowders as raw materials and to study its properties.The MgF2 nanopowders were prepared using chemical precipitation and the translucent ceramics were fabricated by hot-pressing sin
The inlfuence law of clay on mortar lfuidity mixed with polycarboxylate superplasticizer was studied. Several methods of inhibiting clay adsorption of polycarboxylate superplasticizer were discussed. The experimental results show that clay has signiifcant
A method to improve the low-velocity impact performance of composite laminate is proposed,and a multi-island genetic algorithm is used for the optimization of composite laminate stacking sequence under low-velocity impact loads based on a 2D dynamic impac
The dynamic shear modulusG of soil was determined using a dynamic triaxial test system (DTTS) together with a iftting method. First, a novel linear relationship betweenG and damping ratioλ was proposed, which was used to select the appropriate G. Then, a
In order to lower the imidization temperature of polyamic acids (PAA), the catalytic activities of the curing agents p-hydroxybenzoic acid (PHA), quinoline (QL), benzimidazole (BI), benzotriazole (BTA), triethylamine (Et3N) and 1, 8-diazabicyclo [5.4.0]un
The resistivity of Hg0.89Mn0.11Te has been measured by the superconducting quantum interference device magnetometer in the temperature range from 5 to 200 K under the applied magnetic ifeld of 1, 2, 4 and 6.5 Tesla, respectively, compared with that of no-