合成了表面活性剂月桂酸铝[(C11H23COO)3Al],对其与非离子表面活性剂十四烷基二甲基氧化胺(C14DMAO)混合体系在水溶液中的相行为进行了研究,观察到了Lα-相,并利用偏光显微镜(POM)和透射电子显微镜(TEM)确认了多层囊泡的存在.该囊泡相的形成是Al3+的金属配位作用所导致的,此类配位囊泡相可被用作无机纳米材料制备的前驱体.
The surfactant aluminum laurate [(C11H23COO) 3Al] was synthesized and its phase behavior in a mixed solution with nonionic surfactant tetradecyldimethylamine oxide (C14DMAO) was studied. It was observed that Lα - phase and the presence of multilamellar vesicles was confirmed using a polarizing microscope (POM) and a transmission electron microscope (TEM) .The formation of the vesicle phase was caused by the metal coordination of Al3 + Can be used as a precursor for the preparation of inorganic nanomaterials.