Present now the application of microcellular polymeric materials in biomedical field is growing rapidly, as that of guided tissue regeneration and cell transplantation. As far as guided tissue regeneration is concerned, porous implants are used as size selective membrane to promote the growth of a special tissue in a healing site. Ideally, the implant should be inherently biocompatible,have well-defined cell size and be resorbable with appropriate biodegradation rates.Poly(a-caprolactone) (PCL) is a kind of materials suit for the demands above. PCL is biocompatible and biodegradable aliphatic polyester which is nontoxic for living organisms and bioresorbable after a period of implantation. Because of its unique combination of biocompatibility, permeability and biodegradability, PCL and some of its copolymer with lactides and glycolide have been widely applied in medicine as artificial skin, artificial bone and containers for sustained drug release.Goel and Beckman have reported a new method to generate microcellular poly(methy l methacrylate) foams in which the samples are saturated with CO2 under a series of supercritical (SC)conditions, and then the system is rapidly depressurized to atmospheric pressure at constant temperature. Unlike traditional methods, it reduces glass-transition temperature (Tg) of the mixture to below the experimental temperature rather than directly heat the system above Tg. In this process of nucleation, no phase separation occurs as well as no phase boundary meets, so the cellular structure of the foam can be retained better.In this work, we have generated PCL foams by using supercritical CO2. Because of the low glass transition temperature (Tg = -60 ℃) of PCL far below the ice point, the experimental temperature in our study is much higher than Tg, which is different from the studies by others before. A series of variable factors on the foam structure as saturation temperature, saturation pressure, saturation time and depressurization time were studied. The experimental results indicate higher saturation temperature produce reduced bulk densities while holding other variable experimental conditions,and different saturation pressure produce different nucleation process. In addition, saturation time has profound effect on the structure of the product. XRD result shows that the foamed PCL is more inclined to degrade than the original PCL for the reason of its lower crystallinity.