【摘 要】
：
BaTiO3 films on Ti substrate were fabricated by alternative current(AC) and direct current(DC) micro arc oxidation (MAO). Microstructures of films were investig
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
BaTiO3 films on Ti substrate were fabricated by alternative current(AC) and direct current(DC) micro arc oxidation (MAO). Microstructures of films were investigated by means of SEM, XRD and TEM. The results show that the amorphous phase and primitive cubic phase are the main phases in the films prepared by AC MAO. Even after being annealed at 1 200 ℃ for 8 h,only a few tetragonal phases can be observed in films prepared by AC MAO. However, tetragonal BaTiO3 phase can be produced by DC MAO directly. In the films prepared by DC MAO, a mixture of cubic phase and tetragonal phase is formed. After sparking spacious distribution, sparking duration and temperature gradient near sparking sites were taken into account, and a mechanism of synthesis of tetragonal BaTiO3 phase by DC MAO was proposed.
其他文献
To investigate the influence of the solidification on the solder bump formation in the solder jet process, the volume of fluid (VOF) models of the solder drople
A series of the Pt-Sn/SBA-15 catalysts were prepared and their properties characterized by using X-ray powder diffraction(XRD),N2 adsorption-desorption,high res
Novel pyridine-containing macrocyclic compounds, such as 6,12,19,25-tetramethyl-7,11,20,24-dinitrilo-dibenzo[b,m]l,4,12,15-tetra-azacyclodoc osine (TMCD), were
The influence of crystallization on the corrosion behavior of Al86Ni6La6Cu2 amorphous alloy in 0.01 M NaCl solution was inves-tigated by electrochemical techniq
The adsorption properties of a novel gel-type weak acid resin (110-H) for Pb2+ were investigated using chemical methods and IR spectrometry. The optimal adsorpt
Using pressure swing adsorption(PSA)technology to purify carbon monoxide(CO)discharged from industria]gases is a high-efficiency and economicalmethod.In.this ar
As the aircraft and aerospace industry and the automobile industry are developed, the demand of reliable materials with high strength and high toughness is stea
Fluoropolymer and different kinds of silica particles were used for controlling surface chemistry and morphology,respectively. A superhydrophobic surface origin
The effects of BaO addition on the phase composition, relative density and electric conductivity ofxCu/10NiO-NiFe2O4 (x=5, 10) cermets were studied, which were
The aggregated nanorings of EuF3 were synthesized via ultrasonic irritation in aqueous solution. The products were characterized by X-ray powder diffraction (XR