The oxidation behavior of Ni-Cr-Al-Y coating produced by multi-arc ion plating with and without an enamel coating was investigated in flow oxygen and oxygen containing water vapor at 900 ℃. The results show that Ni-Cr-Al-Y coating exhibits low oxidation rate at 900 ℃ in pure oxygen and the oxidation kinetics follow the parabolic rate law. The presence of water vapor accelerates the oxidation rate of Ni-Cr-Al-Y coating and K38G alloy.The enamel top coating is very effective in protecting the Ni-Cr-Al-Y coating from water vapor corrosion attack, but the corrosion attack beneath the enamel coating is not observed.