【摘 要】
：
The effects of Zn content on the as-cast microstructure and mechanical properties of Mg-xZn-4A1 alloys containing TiC and rare earth elements were investigated
【机 构】
：
Chongqing Engineering Research Center for Magnesium Alloys,Department of Materials Science and Engin
论文部分内容阅读
The effects of Zn content on the as-cast microstructure and mechanical properties of Mg-xZn-4A1 alloys containing TiC and rare earth elements were investigated by optical microscopy(OM), scanning electron microscopy(SEM) analysis, X-ray diffraction (XRD) analysis and tensile test. The results show that Zn content which increased from 8% to 12% does not obviously influence on the alloy phase type of the Mg-xZn-4A1 experimental alloys containing 0.25%RE and 1%TiC, but with Zn content increasing from 8% to 12%, the amount of Mg32(Al,Zn)49 phase in the as-cast microstructure of the experimental alloys increases and its distribution becomes more continuous. In addition, the Mg-10Zn-4A1 alloy containing 0.25%RE and 1TiC has the highest ultimate tensile strength at room temperature and 150 ℃ and highest yield strength and elongation at 150 ℃. Furthermore, with Zn content increasing from 8% to 12%, the yield strength and elongation of Mg-xZn-4A1 experimental alloys containing 0.25%RE and 1%TiC increase and decrease at room temperature, respectively.
其他文献
High-resolution X-ray diffractometry (HRXRD) was used to assess the quality of 6H-SiC crystals grown by sublimation method. The results show the occurrence of l
Effects of the process parameters, including deformation temperature, punch velocity and extrusion ratio, on the deformation and microstructure characterization
The nanocrystalline Fe82Nb7B10Cu1 soft magnetic ribbons were treated with the mixture gas flow of ammonia and hydrogen at 673 K. The influence of the nitridatio
This paper reports the influence of heat transfer surface treatment on the formation of calcium sulphate deposit during flow boiling heat transfer. The surface
The alternative heating/cooling cycles(thermal fatigue)of K465 superalloy were carried out. The specimens were held at 1 050 ℃ for 300 s, then quenched into 20
The hot rheological forming method was proposed to form the second titanium alloy vane disk. The hot rheological forming process of the TC11 titanium vane disk
LiFePO4 thin films were prepared by sol-gel technique. The phase and surface morphology were characterized by X-ray diffraction and scanning electron microscopy
In order to solve the reserve stability problem of pyrotechnic explosives containing magnesium powder,a coating method named rapid expansion of supercritical fl
High Nb containing TiAl alloys with nominal composition of Ti-45Al-9(Nb, W, B) were fabricated at different hot pressing temperatures. The experimental results
SCS-6 SiC continuous fiber-reinforced Ti-Al intermetallics-matrix composites were fabricated by HIP method and then heat-treated in vacuum under different condi