The resistivities of vanadium-doped semi-insulating 4H-SiC wafers were measured by a contactless resistivity measurement system. Anomalous resistivity was found in semi-insulating 4H-SiC wafer. Raman spectra of semi-insulating4H-SiC wafer indicated that the anomalous resistivity was caused by polytype inclusion. Based on the activation energies of different SiC polytypes calculated from resistivity versus temperature data measured by COREMA-VT, the resistivities in the vanadium-doped semi-insulating 4H-SiC wafer with 6H polytype inclusion were calculated. The calculated resistivities are quite consistent with the measured resistivities. Furthermore, the compensation mechanism for the formation of anomalous resistivity was proposed.
The resistivities of vanadium-doped semi-insulating 4H-SiC wafers were measured by a contactless resistivity measurement system. Anomalous resistivity was found in semi-insulating 4H-SiC wafer. Raman spectra of semi- Based on the activation energies of different SiC polytypes calculated from resistivity versus temperature data measured by COREMA-VT, the resistivities in the vanadium-doped semi-insulating 4H-SiC wafer with 6H polytype inclusion were calculated. The calculated resistivities are quite consistent with the measured resistivities. Furthermore, the compensation mechanism for the formation of anomalous resistivity was proposed.