本实验利用粉末X射线衍射方法,研究了高压淬火态的EuTbO_3产物。获得了(Eu~(3+)Tb~(3+))O_3单相固溶体新物质及其高温高压合成过程中结构的变化顺序。用振簧式磁强计测得了(EuTb)O_3的室温顺磁磁化率。
In this experiment, the powder X-ray diffraction method was used to study the high-pressure quenched EuTbO_3 product. The order of the structure of (Eu ~ (3 +) Tb ~ (3 +)) O_3 single phase solid solution and its structure during high temperature and high pressure synthesis were obtained. The room-temperature paramagnetic susceptibility of (EuTb) O_3 was measured with a vibrating-spring magnetometer.