为了研制出发泡倍数高、粘度强的有机固化泡沫最佳配方,首先通过分析设计出树脂液、发泡剂组合和树脂液与发泡剂质量比属于3因素3水平、2项考查指标的正交试验表L9(34),分析试验数据得出最佳发泡倍数的组合为A2B3C3或者A3B3C3;最佳粘度的组合为A3B3C3,试验结果表明既要求发泡倍数高又满足粘度强的有机固化泡沫的最佳组合为A3B3C3。
In order to develop a high foaming ratio, high viscosity organic curing foam best formula, first by analyzing the design of the resin solution, blowing agent combination and resin solution and blowing agent quality ratio of 3 factors and 3 levels, two test indicators positive Test table L9 (34), analysis of experimental data to obtain the best combination of foam ratio A2B3C3 or A3B3C3; the best combination of viscosity for the A3B3C3, the test results show that both high foaming multiple and meet the viscosity of the organic curing foam The best combination is A3B3C3.