【摘 要】
：
Nanometer-sized yttrium aluminum garnet (YAG) powders were synthesized by using the coprecipitation method with ammo-nium hydrogen carbonate as a precipitant. T
【机 构】
：
Key Laboratory of Materials Physics
论文部分内容阅读
Nanometer-sized yttrium aluminum garnet (YAG) powders were synthesized by using the coprecipitation method with ammo-nium hydrogen carbonate as a precipitant. The results indicated that an extremely loose YAG precursor was obtained when iodine was intro-duced in the coprecipitation process on the condition that the initial concentrations of y3+ and AI3+ in the solution were set at 0.018 and 0.03 mol/L, respectively, and pH=8. Consequently, the resulting YAG powders after calcination at 1173 K for 2 h were composed of monodis-persed particles with an average grain size of 30 nm and better sinterability. The present results indicated that the modified coprecipitation method, with iodine as an additive, was superior to the conventional coprecipitation method, to synthesize ultrafine YAG powders.
其他文献
As the aircraft and aerospace industry and the automobile industry are developed, the demand of reliable materials with high strength and high toughness is stea
Fluoropolymer and different kinds of silica particles were used for controlling surface chemistry and morphology,respectively. A superhydrophobic surface origin
The effects of BaO addition on the phase composition, relative density and electric conductivity ofxCu/10NiO-NiFe2O4 (x=5, 10) cermets were studied, which were
The aggregated nanorings of EuF3 were synthesized via ultrasonic irritation in aqueous solution. The products were characterized by X-ray powder diffraction (XR
BaTiO3 films on Ti substrate were fabricated by alternative current(AC) and direct current(DC) micro arc oxidation (MAO). Microstructures of films were investig
The influence of strontium(Sr) and rare earth(RE) elements on the corrosion behavior of AZ91D magnesium alloy was investigated by conventional corrosion testing
The operating temperature of a solid oxide fuel cell (SOFC) stack is a very important parameter to be controlled, which impacts the performance of the SOFC due
C/C-SiC braking composites, based on reinforcement of carbon fibers and rnatrices of carbon and silicon carbide, were fabricated by warm compaction and in situ
Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading
The cyclic voltammetry and chronoamperometry were used to study the influence of SiC particles on the nucleation and growth of nickel deposition on copper matri