【摘 要】
：
Based on SIMA, the Al-Si alloy semi-solid billets were successfully fabricated by means of strain inducement and isothermal treatment for AlSi9Mg poured in the
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Based on SIMA, the Al-Si alloy semi-solid billets were successfully fabricated by means of strain inducement and isothermal treatment for AlSi9Mg poured in the range of near-liquidus. Through orthogonal test, the effects of combination action of near-liquidus casting, strain inducement and isothermal treatment on the morphology of primary α-Al phase of AlSi9Mg close to eutectic point were investigated, and the optimal match relation between the processing parameters of solidification, deformation parameters of strain inducement, processing parameters of isothermal treatment and microstructure parameters of semi-solid alloy was established. The results indicate that compared with the single near-liquidus casting or SIMA, the microstructure of primary α-Al phase in AlSi9Mg alloy prepared by compound fabrication process is more homogeneous, with more globular and finer particles,which has average grain size of 40-50 μm and shape factor of greater than 0.75. After holding at 605 ℃ for 30-40 min under a certain cooling rate, increased deformation volume in SIMA benefits the refinement of the grain and the improvement of the morphology for primary phase.
其他文献
Er3+/Yb3+-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature
Based on crystal plasticity theory and surface layer model, relation of flow stress to billet dimension and grain size was built,and rationality of derived rela
The structure defects such as stray grains during unidirectional solidification can severely reduce the performance of single crystal turbine blades. A dendrite
To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress-true strain curves of three kinds of aluminum
The (100)-orientated diamond film was deposited by hot-filament chemical vapor deposition (HFCVD) technology with a positive DC bias voltage. The morphology,X-r
The oxidation behavior of NiTi and NiTiNb alloys containing different amounts of Nb (7%, 9%, mole fraction) were studied at 800 ℃ in air. It is found that the
The tool flank begins to wear out as soon as cutting process proceeds. Cutting parameters such as cutting forces and cutting temperature will vary with increasi
The influences of RE-modification and Sr-modification on the hydrogen content and surface oxide film of A356 aluminum alloy melt were investigated. The hydrogen
为明确杆状病毒几丁质酶对病毒杀虫剂的增效作用,采用PCR扩增获得斜纹夜蛾核型多角体病毒(SpltNPV)不含N-端信号肽序列的几丁质酶基因片段SpltNPVChiA/S-和甜菜夜蛾核型多角
NiAl-0.3Ru and NiAl-30Cr-4Mo alloys were fabricated by arc melting method and then annealed at 1 423 K for 12 h. It has been revealed that NiAl-0.3Ru was in a s