【摘 要】
：
采用气雾化法制备高氮超级奥氏体不锈钢粉末,利用热等静压成形。结果表明,热等静压后,材料完全致密,而σ及Cr2 N两相的析出导致材料塑性、韧性及耐蚀性显著下降。材料经1200
【机 构】
：
钢铁研究总院,安泰科技股份有限公司,
论文部分内容阅读
采用气雾化法制备高氮超级奥氏体不锈钢粉末,利用热等静压成形。结果表明,热等静压后,材料完全致密,而σ及Cr2 N两相的析出导致材料塑性、韧性及耐蚀性显著下降。材料经1200℃×1 h固溶处理后,力学性能及耐蚀性能大大提高,抗拉强度Rm为1050 MPa、屈服强度Rp0.2为735 MPa,伸长率A为57.0%,自腐蚀电位Ecorr为0.946 V。
High-nitrogen super austenitic stainless steel powder was prepared by gas atomization method and was hot isostatic pressing. The results show that the material is completely densified after hot isostatic pressing, and the precipitation of σ and Cr2N phases leads to a significant decrease of plasticity, toughness and corrosion resistance. The mechanical properties and corrosion resistance of the material after 1200 ℃ × 1 h solution treatment were greatly improved. The tensile strength Rm was 1050 MPa, the yield strength Rp0.2 was 735 MPa, the elongation A was 57.0%, the corrosion potential Ecorr 0.946 V.
其他文献
由河北省省会文明办、河北省企业信用促进会石家庄市工委联合组织的石家庄市“善行河北·诚信企业”主题实践活动启动大会7月30日上午在石家庄市总工会大楼召开。全市知名企
北京市政集团第一工程处工会十分注重开展经济技术创新和合理化建议活动,他们在去年承担的北京市政重点工程中尝到了甜头,2003年处工会组织职工结合工程的实际提出并在施工
目的：探讨应用经皮穿刺清理棘球蚴内囊子囊及囊内坏死组织，并对囊腔胆瘘进行处理。方法：采用我们自行设计的专用器械———扩张型多功能套管式穿刺针ＤＭＦＴ（ＤｉｌａｔａｂｌｅＭｕｌｔｙＦｕｎｃｔｉｏｎＴｒｏｃａｒ）对腹腔棘球蚴病应用经皮
目的:研究(１４)Ｃ－尿素呼吸试验（ＵＢＴ）诊断幽门螺杆菌（ＨＰ）感染的应用价值。方法对１１９例有上消化道症状而就医的患者同时做(１４)Ｃ－尿素呼吸试验、快速尿素酶试验（ＲＵＴ）、组织切片Ｗａｒｔｈｉｎ－Ｓｔａｒｒｙ银染色。将上述三种方法的敏
新课标指出:“小学各个年级的阅读教学都要重视朗读。要让学生充分地读,在读中整体感知,在读中有所感悟,在读中培养语感,在读中受到情感的熏陶。”朗读和感悟作为一种简单而
对于在远程教育中提倡更广泛地使用信息与通讯技术的人士,他们往往忽视了考虑现代技术在教、学及管理中运用所面临的特殊挑战。为了帮助人们分析如何在远程教育中恰当地应用
据《The Lancet》1997年350卷第9080期报道 有关炎症性肠病(IBD)的病因,目前尚存争议。有人报道,儿童期感染过麻疹病毒者,其日后患IBD特别是Crohn病的危险性增高。为了了解
对课程领导的研究,已随着基础教育课程的改革和推进,成为一个全新的领域。作为一个新的理念,课程领导更重视合作交流、民主开放。农村幼儿园教育是基础教育的一部分,是基础教
通过最新的全球地磁模型——CALS10K.1b,结合CALS3K.4与IGRF11模型,计算并分析了10000BC~1990AD期间中国大陆及邻近地区非偶极子(ND)磁场Z分量的时空变化。为了深入了解ND场
●首钢第三炼钢厂三好转炉龄突破2.5万炉大关,冶炼合格钢水211.55万吨,创出该厂历史新记录 ●首钢举办“关爱生命、关注安全”宣传日活动
● Shougang No.3 Steelmaking Pl