【摘 要】
：
采用集束拉拔技术和热处理技术制备出了Nb管增强Cu-Nb多芯复合线材,当复合线材线径为?1.7mm时,其抗拉强度接近1.2GPa,导电率为74%IACS。分别对?2.5、?2.2、?2.0、?1.7mm的Cu-
论文部分内容阅读
采用集束拉拔技术和热处理技术制备出了Nb管增强Cu-Nb多芯复合线材,当复合线材线径为?1.7mm时,其抗拉强度接近1.2GPa,导电率为74%IACS。分别对?2.5、?2.2、?2.0、?1.7mm的Cu-Nb-Cu多芯复合线材的形变取向、微观结构及力学性能和导电性能进行了表征。探讨了冷加工变形量对Cu-Nb-Cu多芯复合线材微观组织及性能影响的机理。
Nb-reinforced Cu-Nb multi-core composite wire was prepared by bundling drawing technology and heat treatment technology. When the composite wire diameter was 1.7mm, the tensile strength was close to 1.2GPa and the conductivity was 74% IACS. The deformation orientation, microstructure, mechanical properties and electrical conductivity of Cu-Nb-Cu multi-core composite wires of 2.5, 2.2, 2.0 and 1.7mm were characterized respectively. The mechanism of cold working deformation on the microstructure and properties of Cu-Nb-Cu multi-core composite wire was discussed.
其他文献
我总结了一下,我家的情感教育体现在以下几个方面。一、从不进行精神惩罚这是我们家的一个原则,从不进行精神惩罚,从不给别人难看的脸色,从不用“我不理你”作为对别人错误的
斯坦利的洞大概有三英尺深了,但只是中间挖进去了,四周并没有这么深。太阳刚刚升出地平线,炙热的阳光照在他脸上。他弯腰拿水壶,突然觉得一阵头晕,觉得自己好像快吐了。他喝
全面评论科举制的千秋利弊功过得失,这是一个很大的题目,不是这篇小文所能担纲胜任的。笔者只能在此要而言之,约而言之。 我注意到一个十分有趣的现象:西方各国学者普遍对中
应用题是培养学生的理论联系实际能力的重要形式,此类试题一般都有新颖的生活情景,凸显着鲜明的时代特征;同时,在命题过程中又能把考查的知识与高中数学的许多方面(比如,函数
论阶级分析方法在宪法学中的合理定位童之伟本文着眼于宪法学研究必须坚持党的基本路线，以对阶级分析方法的应用范围、条件及其在传统宪法学中的地位的考察为基础，提出了在新的历史条件下对阶级分析方法在宪法学中的地位进行重新界定的具体设想。宪法学理论应该反映社会...
<正> 近读中华书局校点本《明史》,发现对僧道服色的记载有错误二处,现摘录于兹,试据有关史料加以订正。《明史》卷67《舆服三·僧道服》载:僧通服,洪武十四年定。……道士,常服青法服,朝衣皆赤,道官亦如之。惟道录司官,法服、朝服,绿纹饰金。凡在京道官,红道衣,金襴,木简。在外道官,红道衣,木简,不用金襴。道士,青道服,木简。王鸿绪《明史稿》卷49和清修《续文献通考》卷93的记载,与此略同。其中:
选择Ti--C--Al和Ti--C--Al--CuO两种体系,采用原位反应近液相线铸造技术,制备铝基复合材料.通过金相显微镜、扫描电镜和X射线衍射仪研究了复合材料的微观组织.对上述两种体系
函数是高中数学主要内容,涉及函数的应用问题,题源丰富、背景深刻、题型新颖、解法灵活,是历年高考的热点之一.有很多应用题涉及到“方案最优化”问题,其解决方法一般是建立
我公司的回转窑规格为φ4.5m×110m,其倾斜角一期为3.5%,二期为4%。回转窑窑体窜动造成的危害有:(1)回转窑机头、机尾密封件的不均匀磨损,密封失效,造成能源损耗、物料泄漏、
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.