【摘 要】
：
A two-component waterborne polyurethane (2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for
【机 构】
：
Department of Chemistry and Chemical Engineering,Institute of Chemical Engineering
论文部分内容阅读
A two-component waterborne polyurethane (2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU particles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI isocyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction between HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on pefformance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.
其他文献
Honeycomb-like superstructures consisting of ZnS nanosheets with uniform thickness of about 20nm and lateral dimension of several micrometers were built up from
For large-sized AISI P20 steel block used as plastic die with a thickness of more than 200 mm, appropriate quenching processes are the key to obtain much thick
Mg65Cu25Gd10 amorphous alloy powders were synthesized by mechanical alloying (MA). The most suitable process is that the milling velocity is 600 r/min and the m
The evolution of configurations of Aln (n=3,4,6,13,19) clusters were investigated using linear synchronous transit (LST) method. The stable structures of Al3,Al
Under electron beam irradiation, the in-situ formation of 2H-SiC dentritic nanocrystals from amorphous silicon carbide at room temperature was observed. The hom
Thin films of Nd3+/V5+-cosubstituted bismuth titanate,(Bi3.5Nd0.5)( Ti2.96V0.04)O12 (BNTV),were fabricated on the Pt(111)/Ti/SiO2/Si(100) substrates by a chemic
Comparing and analyzing some volume deformation measuring means for cement-based materials at home and abroad, a continuous online monitor of cement-based mater
The aim of this study is to show how fractal analysis can be effectively used to characterize thetexture of porous solids.The materials under study were carbon
This study describes the development of novel protocols extending the real-time ultrasonic reflectometry(UTDR) for the detection of membrane fouling in hollow f
A new inverse method by coupling iSIGHT and ABAQUS was proposed to determine the constitutive parameters of Al2O3sf/LY12 composite deforming at elevated tempera