A new metastable beta titanium alloy of Ti-Al-Mo-V-Cr-Fe-Zr-Sn system was designed and named Ti-B20. In order to investigate the aging properties and microstruc
【机 构】
：
Northwest Institute for Non-ferrous Metal Research,School of Materials Science and Engineering
论文部分内容阅读
A new metastable beta titanium alloy of Ti-Al-Mo-V-Cr-Fe-Zr-Sn system was designed and named Ti-B20. In order to investigate the aging properties and microstructures of the new alloy subjected to different solution treatments, the tensile and Vickers hardness tests were carried out and the optical microscope and scanning electron microscope analysis were performed. The results show that the new alloy displays rapid aging response, high age strengthening effect and fine deposition. In addition, beta solution results in ultra high age hardening effect with low tensile ductility, whereas excellent combination of aging strength and ductility can be obtained after solution treated below beta transus temperature.
其他文献
The existence of yttrium in Ti-23Al-25Nb alloy and its influence on the microstructure after heat treatment of Ti-23Al-25Nb alloy were investigated using therma
Dipolar relaxation and dielectric/piezoelectric resonance in a (001)-cut Pb(Zn1/3Nb2/3)0.9Ti0.1O3 (PZNT10%) single crystal before and after electric (E)-field p
Three different coatings, Cr, SiO2/Cr and HfO2/SiO2 were deposited by electron beam physical vapor deposition (EB-PVD). Relevant composition and mechanical prop
A novel Al-based composite material (Al63Cu25Fe12)p/A356 was prepared by spray co-deposition. It is revealed that the reinforcement of Al63Cu25Fe12 quasicrystal
The corrosion behavior of a CuCrNiAl alloy in HCl solutions was studied by means of metallograph, XRD, SEM/EDX and TEM methods. The results show that in low con
Current—voltage (I—V) and capacitance-voltage (C—V) characteristics of Au/p-CZT contacts with different surface treatments on cadmium zinc telluride (CZT) wa
Compositional graded BaxSr1-xTiO3 (x=0.6,0.7,0.8,0.9,1.0) (BST) thin films (less than 400 nm) were fabricated on Si and Pt/Ti/SiO2/Si substrates by sol-gel tech
Low temperature sintering NiCuZn ferrite was employed at most cases due to its co-firability with Ag (below 960 ℃). The NiCuZn ferrite sintered body with high-
The carbon nanotube (CNT) growth of iron oxide-deposited trench-patterns and the locally-ordered CNT arrays on silicon substrate were achieved by simple thermal
Electrochemical methods were applied to investigate the corrosion behaviour of LY12CZ under applied stress in 3% sodium chloride aqueous solution. The experimen