The HA/UHMWPE nanocomposite is compounded by twin-screw extrusion of the HA and UHMWPE powder mixture in paraffin oil and then compression molded to a sheet form. TGA measurement shows the HA weight loss after processing is about 1%-2%. FTIR spectra indicate the paraffin oil residue is trivial and UHMWPE is not oxidized. SEM reveals the HA nano particles are homogeneously dispersed by twin-screw extrusion and the inter-particle spaces are penetrated with UHMWPE fibrils by swelling treatment. HRTEM image indicates the HA particles and UHMWPE are intimately contacted by mechanical interlocking. Compared with the unfilled UHMWPE, stiffness of the composite with the HA volume fraction 0.23 was significantly enhanced to 9 times without detriment of the yield strength and the ductility.
The HA / UHMWPE nanocomposite is compounded by twin-screw extrusion of the HA and UHMWPE powder mixture in paraffin oil and then compression molded to a sheet form. TGA measurement shows the HA weight loss after processing is about 1% -2%. FTIR spectra indicate the paraffin oil residue is trivial and UHMWPE is not oxidized. SEM reveals the HA nano particles are homogeneously dispersed by twin-screw extrusion and the inter-particle spaces are penetrated with UHMWPE fibrils by swelling treatment. HRTEM image indicates the HA particles and UHMWPE Compared in the unfilled UHMWPE, stiffness of the composite with the HA volume fraction 0.23 was significantly enhanced to 9 times without detriment of the yield strength and the ductility.